category：Building materials / date：2023-01-27 01:22:42 / browse：117 / comment：3
Zinc layer thickness: there is a great difference between cold galvanized square pipe and hot galvanized square pipe in galvanizing process; Cold galvanized square pipes are prone to & ldquo; Electric burning & rdquo; The color of this part is gray and the zinc layer is thick. It is easy to form a current dead angle at the corner, resulting in an under current area. The zinc layer at this part is thin, and there is no zinc layer attached to the cold galvanized square pipe. The cold galvanized square pipe has no zinc lump and caking as a whole, but the overall zinc layer is thin, and the thickness of the outer wall zinc layer is μ m-μ m. The and outer walls of the hot-dip galvanized square tube are attached with zinc layer, and there will be water marks and a few zinc tumors, but the overall zinc layer is thick, and the thickness of the zinc layer on the inner and outer walls of the square tube is -mu; M above. The nature of QB square tube!The inspection items, sampling quantity sampling position and test of square tube shall be in accordance with the provisions of corresponding product standards. With the consent of the demander, hot-rolled square tubes can be sampled in batches according to the rolled root array.Sun Pange,Strength refers to the function that the square tube data is destroyed under static load (appropriate amount of plastic deformation or fracture), because the action form of load includes tension, compression, meandering shear and so on, compressive strength, flexural strength, shear strength and so on. There is often a definite connection between various strengths. In normal use, and double the number of samples shall be taken from the same batch of square tubes for re inspection of unqualified items. If the re inspection results (including any index required by the test of the project) are unqualified, the batch of square tubes shall not be delivered. If the following inspection items fail to pass the preliminary inspection, re inspection is not allowed: A. There are white spots in the low magnification; b. Microscopic.Sunbury,The local heat release in the welding process of square tube can reduce the heat affected zone, avoid the micro of thermal sensitive materials,Sun PangeWhere are galvanized square tubes,Sun PangeSquare tube galvanizing plant, and maintain the properties of materials.There are many processing technologies for square tubes. I won't introduce the specific processing technology here. We only know about the processing technology of each other's tubes. We may have insufficient understanding of its heating technology. Next, I'll give you a detailed introduction to the heating technology of the lower tubes.Forging square tube: a kind of pressure processing in which the reciprocating impact force of the forging hammer or the pressure of the press changes the blank into the shape and size we need. It is generally divided into forging and die forging. It is often used to produce large-scale materials and materials with large square tube size.
Oil drilling pipe (yb-) is a square pipe used for internal or external thickening at both ends of oil drilling. Steel pipes are divided into turning wire and non turning wire. Turning wire pipe is connected with joint, and non turning wire pipe is connected with tool joint by butt welding.D. do not cut your hands boring, especially for girls. Holding or fingers will bind themselves.The inspection items, sampling quantity, sampling position and test of square tube shall be in accordance with the provisions of corresponding product standards. With the consent of the demander, hot-rolled square tubes can be sampled in batches according to the rolled root array.Highly recommended,Sun PangeOf hot dip galvanized square pipe,Square tube, modified square tube, square tube QB square tube and hot-rolled square tube are qualified in quality inspection. The manufacturer adopts advanced equipment to ensure the quality of each product. Magnetic flux leakage testing for surface defects of square tubes is very similar to magnetic particle testing for square tubes, and its scope of application, sensitivity and reliability are stronger than magnetic particle testing. Indirect square forming process the traditional forming process of cold-formed square pipe is to gradually roll the hot-rolled steel coil multi stand forming unit into round pipe at room temperature, and then the shaping unit will roll the round pipe into square pipe, which is called indirect square forming process. The traditional roll forming process uses the method of fixed bending point position and variable bending radian to complete the corner forming of pipe blank, which is suitable for rolling small and medium-sized products. Rolling with this process & ldquo; Superb & rdquo; Square tube will show its inherent defects. Because the roll work in the bending process of this process is always concentrated at the point, excessive stress concentration often shows microcracks in the bending process of profiles, which will lead to cracking in serious cases. The products with such defects have serious consequences when they are used in building steel structures. The study of the broken square tube column in the Hanshin earthquake in Japan shows that the corner microcrack is the main cause of the square tube fracture. At the same time, due to the different forming bending radians of products with different wall thickness the universality of rolls is limited. The large-size cold-formed square tube used in the process adopts the advanced & ldquo; Direct Square & rdquo; The production process is to directly roll the hot-rolled steel coil into a square and rectangular shape at room temperature.The strength, plasticity and hardness discussed above in fatigue QB are the indicators of the mechanical properties of metals under static load. In fact, under which fatigue will occur.Classification of square pipe material square pipe is divided into ordinary carbon steel square pipe and low alloy square pipe according to material. Ordinary carbon steel is divided into Q Q q SS # steel, # steel, etc; Low alloy steels are divided into q Mn, Q, St-, etc.
B. spring steel C. bearing steel tool steel: A. carbon tool steel; b. Alloy tool steel; c. High speed tool steel.Good quality,With the improvement of production quality, the quality of square tubes is getting better and better. The quality of square tubes will affect our lives. Because the functions of square tubes are different, their characteristics and uses are different. I will introduce the characteristics and uses of square tubes in detail.The painting of the square tube has to go through a process, which requires us to conduct comprehensive consideration and analysis. In particular, the quality and level of the paint and the relevant technical level deserve our attention. Note that the square tube should not be used immediately after painting, but should be placed for a period of time and wait until the paint is dry!After cold drawing and aging treatment, the yield point is improved, the tensile ultimate strength is also increased, and the plasticity continues to decrease. Due to the reduction of internal stress during aging, the modulus can be basically restored. According to this principle, cold drawing or cold drawing of reinforcement or low carbon steel wire rod is often carried out on site or prefabricated component factory, so as to improve yield strength and save steel.Sun Pange,Derusting grade for the construction process of epoxy, ethylene, phenolic and other coatings commonly used for square pipes, the surface of square pipes is generally required to reach near white grade (SA). Practice has proved that almost all oxide scale, rust and other dirt can be removed by using this derusting grade, and the depth of anchor grain can reach ~ & mu; m, which fully meets the requirements of adhesion between layer and square pipe The shot derusting process can meet the technical conditions of near white level (SA) with low operation cost and stable and reliable quality.The difference between square pipe and seamless steel pipe the main feature of seamless steel pipe is no welding joint and can withstand large pressure. The product can be very rough as cast or cold drawn parts.Forging square tube: a kind of pressure processing in which the reciprocating impact force of the forging hammer or the pressure of the press changes the blank into the shape and size we need. It is generally divided into forging and die forging. It is often used to produce large-scale materials and materials with large square tube size.
share 3 Comments
Comment / Cancel reply